Characterization of Membrane of Poly (L,co-D,L-lactic acid-co-trimethylene carbonate) (PLDLA-co-TMC) (50/50) loaded with Silk Fibroin
Co-Authors
Article Reviewed By:
Qiqing Zhang(zhangqiq@126.com)
Marzio Sorlini(marzio.sorlini@supsi.ch)
F Guillermo D(fgb@um.es)
Pranab Goswami(pgoswami@iitg.ernet.in)
Citation
Marco Vin
Abstract
Silk produced by Bombyx-mori consists of two proteins sericin and fibroin. Silk Fibroin (SF) an attractive material for epithelial tissue regeneration. The aim of this study was to characterize membranes of PLDLA-co-TMC/SF once it could be used as a wound dressing to burn treatment and epithelial tissue regeneration. Membranes of Poly(L-co-D,L-lactic acid-co-TMC)/SF were prepared by casting and it was analysed by: FTIR - there was no change in the PLDLA-co-TMC spectrum after SF be added in this polymer, Swelling Test – the samples with 5% SF had a different swelling behaviour of PLDLA-co-TMC. Membrane with 5% SF showed swelling rate faster than PLDLA-co-TMC. Contact angle measurement - PLDLA-co-TMC (50/50) showed a contact angle value higher than samples with SF. SEM – the addition of SF in PLDLA-co-TMC apparently leaves the polymer surface more roughened. Tensile test - there was a decrease in the Young\'s modulus and there was an increase in the elongation at break of PLDLA-co-TMC/SF, DSC – SF did not change the glass temperature (Tg) of PLDLA-co-TMC. The membrane of PLDLA-co-TMC/SF was characterized and it has potential to be used as a wound dressing to burn treatment and epithelial tissue regeneration.
References
Altman, G. H.; Diaz, F.; Jakuba, C.; Calabro, T.; Horan, R. L.; Chen, J.; Lu, H.; Richmond J.; Kaplan, D. L. Biomaterials, 2003, 24, 401-416. 00353-8
View ArticleSantin, M.; Motta, A.; Freddi, G.; Cannas, M. J. Biomed. Mater. Res., 1999, 9, 382-389. 1097-4636(19990905)46:3<382::AID-JBM11>3.0.CO;2-R
View ArticleLi, M.; Lu, S.; Wu, Z.; Tan, K.; Minoura, N.; Kuga, S. Int. J. Biol. Macromol., 2002, 30, 89-94. 00007-7
View ArticleLi, M. Z.; Ogiso, M.; Minoura, N. Biomaterials, 2003, 24, 357-365. 00326-5
View ArticleMeinel, L.; Hofmann, S.; Karageorgiou, V.; Kirker-Head, C.; McCool, J.; Gronowicz, G.; Zichner, L.; Langer, R.; Vunjak-Novakovic, G.; Kaplan, D. L. Biomaterials, 2005, 26, 147-155. PMid:15207461
View Article PubMed/NCBIBadami, A. S.; Kreke, M. R.; Thompson, M. S.; Riffle, J. S.; & Goldstein, A. S. Biomaterials, 2006, 27, 596-606. PMid:16023716
View Article PubMed/NCBILiang, D.; Hsiao, B. S.; Chu, B. Adv. Drug Deliver. Rev., 2007, 59, 1392-1412. PMid:17884240 PMCid:PMC2693708
View Article PubMed/NCBILovett, M.; Eng, G.; Kluge, J. A.; Cannizzaro, C.; Vunjak-Novakovic, G.; Kaplan, D. L. Organogenesis, 2010, 6, 217-224. PMid:21220960 PMCid:PMC3055647
View Article PubMed/NCBILeal-Egana, A.; Scheibel, T. Biotechnol. Appl. Bioc., 2010, 55,155-167. PMid:20222871
View Article PubMed/NCBIQu, Y.; Yang, Y.; Li, J.; Chen, Z.; Li, J.; Tang, K.; Man, Y. J. Biomater. Appl., 2011, 26, 311?325. PMid:20566653
View Article PubMed/NCBIZhang, K.; Wang, H.; Huang, C.; Su, Y.; Mo, X.; Ikada, Y. J. Biomed. Mater. Res. Part A, 2009, 93, 984-993.
Vachiraroj, N.; Ratanavaraporn, J.; Damrongsakkul, S.; Pichyangkura, R.; Banaprasert, T.; Kanokpanont, S. Int. J. Biol. Macromol., 2009, 45, 470-477. PMid:19660495
View Article PubMed/NCBIElia, R.; Newhide, D. R.; Pedevillano, P. D.; Reiss, G. R.; Firpo, M. A.; Hsu, E. W.; Kaplan, D. L.; Prestwich, G. D.; Peattie, R. A. J. Biomater. Appl., 2013, 27,749-762. PMid:22090427
View Article PubMed/NCBIKundu, J.; Poole-Warren, L. A.; Martens, P.; Kundu, S. C. Acta Biomaterialia, 2012, 8, 1720-1729. PMid:22285428
View Article PubMed/NCBIRasal, R. M.; Janorkar, A. V.; Hirt, D. E. Prog. Polym. Sci., 2010, 35, 338-356.
View ArticleZhang, Z.; Kuijerb, R.; Bulstrab, S. K.; Grijpmaa, D. W.; Feijen, J. Biomaterials, 2006, 27, 17411748.
Motta, C. A.; Duek, E .A. R. Mater. Res., 2014, 17, 619-626.
View ArticleRockwood, D. N.; Preda, R. C.; Y?cel, T.; Wang, X.; Lovett, M. L.; Kaplan, D. L. Nature Protocols, 2011, 6, 1612-1631. PMid:21959241 PMCid:PMC3808976
View Article PubMed/NCBISionkowska, A.; Lewandowska, K.; Michalska, M.; Walczak, M. J. Mol. Liq., 2016, 215, 323-327.
View ArticleWang, J.; Yang, Q.; Cheng, N.; Tao, X.; Zhang, Z.; Sun, X.; Zhang, Q. Mater. Sci. Eng. C: Materials for Biological Applications, 2016, 61, 705?711. PMid:26838900
View Article PubMed/NCBIBhardwaj, N.; Rajkhowa, R.; Wang, X.; Devi, D. Int. J. Biol. Macromol., 2015, 81, 31-40. PMid:26226458
View Article PubMed/NCBIMoraes, M. A.; Nogueira, G. M.; Weska, R. F.; Beppu, M. M. Polymers, 2010, 2, 719-727.
View ArticleZhu, H.; Liu, N.; Feng, X.; Chen, J. Mater. Sci. Eng. C: Materials for Biological Applications, 2012, 32, 822-829.
View ArticleFreddi, G.; Pessina, G.; Tsukada, M. Int. J. Biol. Macromol., 1999, 24, 251-263. 00087-7
View ArticleFerri, J. M.; Garcia-Garcia, D.; S?nchez-Nacher, L.; Fenollar, O.; Balart, R. Carbohyd. Polym., 2016, 147, 60-68. PMid:27178909
View Article PubMed/NCBI